Epibond 100 A/B Epibond® 100 A/B High-temperature Epoxy Adhesive |
Epibond 156-1 A/B Epibond® 156-1A/B "Wipe-on" Paste Epoxy Adhesive |
Epibond 420 A/B Epibond® 420 A/B Toughened Epoxy Adhesive |
Epibond 1210 A/B Epibond® 1210 A/B Multi-Purpose Epoxy Adhesive |
Epibond 1210 A/ 9615-A Epibond® 1210 A/9615 A Multi-Purpose Epoxy Adhesive |
|||||
Description | N/A Two-component, heat-curing epoxy structural adhesive designed for demanding applications requiring high hot / wet Tg performance, and elevated temperature performance. | N/A Easy-to-apply, off-white epoxy paste with good electrical properties and adhesion. Particularly suitable as pore filler for composite, plastic and wood surfaces. | N/A Durable, tough, high-strength, blue-green epoxy adhesive suitable for a wide variety of metal, honeycomb and composite bonding applications. | N/A Non-flow, room-temperature cure, tan epoxy adhesive with a long work life. Its low outgassing properties make it particularly suitable for spacecraft applications. | N/A Versatile, tan epoxy adhesive that cures at room temperature and can withstand exposure to jet fuel and water. For bonding metal, wood, glass, ceramics and plastics. | |||||
Test Method for Appearance | N/A | |||||||||
Epibond® 200 A Resin Appearance | N/A | |||||||||
Epibond® 200 B Hardener Appearance | N/A | |||||||||
Mixed System Appearance | N/A | |||||||||
Epibond® 200 A Resin Density | N/A | |||||||||
Epibond® 200 B Hardener Density | N/A | |||||||||
Mixed System Density | N/A | |||||||||
Epibond® 200 A Resin Viscosity at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Epibond® 200 B Hardener Viscosity at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Mixed System Viscosity at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Parts by Weight for Epibond® 200 A Resin | N/A | |||||||||
Parts by Weight for Epibond® 200 B Hardener | N/A | |||||||||
Parts by Volume for Epibond® 200 A Resin | N/A | |||||||||
Parts by Volume for Epibond® 200 B Hardener | N/A | |||||||||
Lap Shear Strength Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 2 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 6 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 7 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 8 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 3 Days Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 7 Days Cure Time | N/A | |||||||||
Lap Shear Strength at 150 Degree Fahrenheit (ºF) (66 Degree Celsius (ºC)) Temperature and 2 Hour Cure Time | N/A | |||||||||
Lap Shear Strength Aging Time at 302 Degree Fahrenheit (ºF) (150 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 0 Days Aging at -55 Degree Fahrenheit (ºF) (-67 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 12 Days Aging at -55 Degree Fahrenheit (ºF) (-67 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 40 Days Aging at -55 Degree Fahrenheit (ºF) (-67 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 50 Days Aging at -55 Degree Fahrenheit (ºF) (-67 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 0 Days Aging at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 12 Days Aging at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 40 Days Aging at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 50 Days Aging at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 12 Days Aging at 200 Degree Fahrenheit (ºF) (93 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 40 Days Aging at 200 Degree Fahrenheit (ºF) (93 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 50 Days Aging at 200 Degree Fahrenheit (ºF) (93 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 0 Days Aging at 400 Degree Fahrenheit (ºF) (204 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 12 Days Aging at 400 Degree Fahrenheit (ºF) (204 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 40 Days Aging at 400 Degree Fahrenheit (ºF) (204 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Lap Shear Strength After 50 Days Aging at 400 Degree Fahrenheit (ºF) (204 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Appearance | N/A | N/A Soft Paste | N/A Semi-Paste | N/A Semi-Paste | N/A Paste | |||||
Test Method for Viscosity at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Viscosity at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Test Method for Density | N/A | |||||||||
Density | N/A | |||||||||
Note for Typical Properties | N/A | |||||||||
Processing | N/A | |||||||||
Mix Ratio by Weight (Part A/Part B) | N/A | |||||||||
Mix Ratio by Volume (Part A/Part B) | N/A | |||||||||
Note for Mix Ratio | N/A | |||||||||
Work Time | N/A | |||||||||
Gel Time 125 Gram (g) at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Typical Cure Cycles | N/A | |||||||||
Note for Typical Physical Properties | N/A | |||||||||
Tensile Strength | N/A | |||||||||
Test Method for Tensile Strength | N/A | |||||||||
Tensile Modulus | N/A | |||||||||
Test Method for Tensile Modulus | N/A | |||||||||
Elongation at Tensile Break | N/A | |||||||||
Test Method for Elongation at Tensile Break | N/A | |||||||||
Compressive Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Compressive Strength at 250 Degree Fahrenheit (ºF) (121 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Compressive Strength at 250 Degree Fahrenheit (ºF) (121 Degree Celsius (ºC)) after 7 days at 160 Degree Fahrenheit (ºF) (71 Degree Celsius (ºC)) and 85% Relative Humidity (RH) | N/A | |||||||||
Test Method for Hardness | N/A | |||||||||
Hardness | N/A | |||||||||
Test Method for T-Peel Strength | N/A | |||||||||
T-Peel Strength1 | N/A 22 lb/in | N/A | N/A | N/A | N/A | |||||
Glass Transition Temperature, Tg, (E' Onset) Cured 5 days at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Glass Transition Temperature, Tg, (E' Onset) Cured 1 Hour at 150 Degree Fahrenheit (ºF) (66 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Test Method for Tensile Lap Shear Strength | N/A | |||||||||
Tensile Lap Shear Strength for Etched and Primed Aluminum Tested at -94 Degree Fahrenheit (ºF) (-70 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength for Etched and Primed Aluminum Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength for Etched and Primed Aluminum Tested at 250 Degree Fahrenheit (ºF) (121 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength for Etched and Primed Aluminum Tested at 350 Degree Fahrenheit (ºF) (177 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength for Etched and Primed Aluminum Tested at 400 Degree Fahrenheit (ºF) (204 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength After 7 Days for Etched and Primed Aluminum Tested at 160 Degree Fahrenheit (ºF) (71 Degree Celsius (ºC)) Temperature and 85 % Relative Humidity (RH) | N/A | |||||||||
Tensile Lap Shear Strength for Anodized and Primed Aluminum (Fluid Resistance) Cure for 7 Days Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength After 7 Days for in Water Anodized and Primed Aluminum (Fluid Resistance) Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength After 7 Days in IPA for Anodized and Primed Aluminum (Fluid Resistance) Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength After 7 Days n Hydraulic Fluid for Anodized and Primed Aluminum (Fluid Resistance) Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength After 7 Days in Jet A for Anodized and Primed Aluminum (Fluid Resistance) Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Lap Shear Strength for Carbon Fiber Reinforced Polymer (CFRP) Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 4 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 5 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 6.5 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 15 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 24 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 120 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Tensile Shear Strength at 73 Degree Fahrenheit (ºF) (23 Degree Celsius (ºC)) Temperature for 168 Hour Cure Time (Aluminum to Aluminum) | N/A | |||||||||
Note for Cure Time | N/A | |||||||||
Width/Diameter | N/A | |||||||||
Number of Elements at 0.20 Inch (in) Width/Diameter | N/A | |||||||||
Number of Elements at 0.21 Inch (in) Width/Diameter | N/A | |||||||||
Nordson EFD Part # at 0.20 Inch (in) Width/Diameter | N/A | |||||||||
Nordson EFD Part # at 0.21 Inch (in) Width/Diameter | N/A | |||||||||
Sulzer Mixpac Part # at 0.21 Inch (in) Width/Diameter | N/A | |||||||||
Note for Static Mixing Nozzles | N/A | |||||||||
Gel Time at 77 Degree Fahrenheit (ºF) Temperature | N/A | |||||||||
Test Method for Tensile Lap Shear Strength Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature for Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength at 180 Degree Fahrenheit (ºF) (82 Degree Celsius (ºC)) Temperature for Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength at 250 Degree Fahrenheit (ºF) (121 Degree Celsius (ºC)) Temperature for Aluminum to Aluminum | N/A | |||||||||
Test Method for Compressive Strength | N/A | |||||||||
Compressive Strength at 180 Degree Fahrenheit (ºF) (82 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Test Method for Elongation | N/A | |||||||||
Elongation | N/A | |||||||||
Test Method for Flexural Strength | N/A | |||||||||
Flexural Strength | N/A | |||||||||
Test Method for Flexural Modulus | N/A | |||||||||
Flexural Modulus | N/A | |||||||||
Glass Transition Temperature, Dynamic Mechanical Analysis (DMA), E' Onset | N/A | |||||||||
Test Method for Insert Shear Strength | N/A | |||||||||
Insert Shear Strength As cured | N/A | |||||||||
Insert Shear Strength as Cured Plus 30 days at 140 Degree Fahrenheit (ºF) (60 Degree Celsius (ºC)) Temperature, 95% Relative Humidity (RH) | N/A | |||||||||
Test Method for Color | N/A | |||||||||
Test Method for Viscosity at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Viscosity at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Test Method for Work Life, 100g at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) | N/A | |||||||||
Mix Ratio | N/A | |||||||||
Work Life, 100 Gram (g) Mass at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Cure Schedule | N/A | |||||||||
Tensile Lap Shear Strength at -67 Degree Fahrenheit (ºF) (-55 Degree Celsius (ºC)) Temperature for Aluminum to Aluminum | N/A | |||||||||
Test Method for Tensile Lap Shear Strength After Seven Days | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature JP-4 Fuel Immersion | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature TT-S-735 Type III Test Fluid | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature Distilled Water | N/A | |||||||||
Note for Typical Cured Properties | N/A | |||||||||
Application | N/A | |||||||||
Work Life, 100 Gram (g) Mass at 25 Degree Celsius (ºC) Temperature | N/A | |||||||||
Tensile Lap Shear Strength at -55 Degree Celsius (ºC) Temperature for Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength at 25 Degree Celsius (ºC) Temperature for Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength at 83 Degree Celsius (ºC) Temperature for Aluminum to Aluminum | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 25 Degree Celsius (ºC) Temperature TT-S-735 Type III Test Fluid | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 25 Degree Celsius (ºC) Temperature JP-4 Fuel Immersion | N/A | |||||||||
Tensile Lap Shear Strength After Seven Days at 25 Degree Celsius (ºC) Temperature Distilled Water | N/A | |||||||||
Mixed Flow, Tested at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature2 | N/A | |||||||||
Extrusion Rate at 70 Pound per Square Inch (psi)3 | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 3 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 4 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature and 5 Hour Cure Time | N/A | |||||||||
Lap Shear Strength at 135 Degree Fahrenheit (ºF) (57 Degree Celsius (ºC)) Temperature and 30 Minute (min) Cure Time | N/A | |||||||||
Note for Handling Strength | N/A | |||||||||
Gel Time 100 Gram (g) at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature | N/A | |||||||||
Original Equipment Manufacturer (OEM) Specifications | N/A Huntsman standard certification | N/A Huntsman standard certification | N/A Boeing BMS 5-107, Cl 1, REV B /Triumph TCE-M-20710-4, Ty 1, REV B | N/A Sundstrand CM 34.40-38-01, REV 3 | N/A Lockheed Martin LAC 30-4639-0100, REV H | |||||
Mix Ratio Ritt by Weight | N/A 100:44 | N/A 100:60 | N/A 100:40 | N/A 100:65 | N/A 100:65 | |||||
Mixed Viscosity at 77 Fahrenheit (ºF) Temperature | N/A 280,000 cP | N/A | N/A | N/A | N/A | |||||
Minimum Gel Time/Pot Life at 77 Fahrenheit (ºF) Temperature | N/A 135-145 (150 gram mass) minutes | N/A 20-50 (100 gram mass) minutes | N/A 60 (100 gram mass) minutes | N/A 50-75 (100 gram mass) minutes | N/A 50-75 (100 gram mass) minutes | |||||
Suggested Cure Schedule Fahrenheit (ºF) | N/A 1 hour at 150 ºF + 3-5 hours at 200 ºF | N/A 3 days at 77 ºF or 1-3 hrs at 150 ºF | N/A 7 days at 77 ºF or 1 hr at 250 ºF | N/A 48 hrs at 77 ºF or 2 hrs at 150 ºF | N/A 48 hrs at 77 ºF or 3 hrs at 150 ºF | |||||
Maximum Service Temperature | N/A 300 ºF | N/A 200 ºF | N/A 150 ºF | N/A Not Determined | N/A Not Determined | |||||
Lap Shear Strength at 77 Fahrenheit (ºF) Temperature (Aluminum to Aluminum) | N/A 5,000 psi | N/A 2,000 psi | N/A 4,500 psi | N/A 2,500 psi | N/A 2,500 psi | |||||
Lap Shear Strength at 180 Fahrenheit (ºF) Temperature (Aluminum to Aluminum) | N/A 4,000 psi | N/A 1,950 psi | N/A 500 psi | N/A 500 psi | N/A | |||||
T-Peel Strength (Roller Peel) | N/A | |||||||||
Flame Retardant | N/A No | |||||||||
Packaging | N/A 50-ml, 200-ml 2:1 dual cartridges | N/A Working packs | N/A 50 ml cartridge and working packs | N/A Working packs | N/A Working packs | |||||
Features | N/A | |||||||||
Applications | N/A | |||||||||
Storage | N/A | |||||||||
Precautionary Statement | N/A | |||||||||
Note | N/A | |||||||||
Color | N/A Off-White | N/A Off-White | N/A Blue-Green | N/A Tan | N/A Tan | |||||
|