LORD® 403, 406 and 410 acrylic adhesives in combination with LORD® Accelerator 19 or 19GB can be used to replace welding, brazing, riveting and other mechanical fastening methods. These adhesives perform particularly well in low-temperature environments and applications that are subject to high impact or high peel loads. LORD® 403, 406 and 410 acrylic adhesives provide a range of working times to accommodate a wide variety of process requirements.
Unit of Measure
Specifications
|
Typical Properties
|
Typical Properties of Adhesive Mixed with Recommended Accelerator
|
Typical Cured Properties
|
Bond Performance LORD® 406 Adhesive/LORD Accelerator 19
|
Shelf Life/Storage
|
Features
|
Applications
|
Additional Information
Specifications
Adhesive Type |
N/A Acrylic |
Cure Time at Room Temperature (RT) for Metal Lap Shears |
N/A 24 hour |
Color |
N/A Off-white to Tan |
Typical Properties
Appearance |
N/A Paste |
Brookfield Viscosity at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature |
N/A 100000 to 300000 cP |
Density |
N/A 9.10 to 9.70 lb/gal1090 to 1162 kg/m³ |
Flash Point Temperature |
N/A 59 ºF15 ºC |
Note for Typical Properties |
N/A Data is typical and not to be used for specification purposes. |
Typical Properties of Adhesive Mixed with Recommended Accelerator
Mix Ratio by Weight for Adhesive to Accelerator A19 |
N/A 3.02:1 |
Mix Ratio by Weight for Adhesive to Accelerator A19 Black |
N/A 3.00:1 |
Mix Ratio by Weight for Adhesive to Accelerator A19GB |
N/A 2.91:1 |
Mix Ratio by Weight for Adhesive to Accelerator A19GB Red |
N/A 2.91:1 |
Mix Ratio by Weight for Adhesive to Accelerator A19GB Gray |
N/A 2.85:1 |
Mix Ratio by Volume for Adhesive to Accelerator A19 |
N/A 4:1 |
Mix Ratio by Volume for Adhesive to Accelerator A19 Black |
N/A 4:1 |
Mix Ratio by Volume for Adhesive to Accelerator A19GB |
N/A 4:1 |
Mix Ratio by Volume for Adhesive to Accelerator A19GB Red |
N/A 4:1 |
Mix Ratio by Volume for Adhesive to Accelerator A19GB Gray |
N/A 4:1 |
Solids Content |
N/A 100 % |
Working Time at 75 Degree Fahrenheit (ºF) (24 Degree Celsius (ºC)) Temperature |
N/A 6 to 10 minutes |
Time to Handling Strength at 75 Degree Fahrenheit (ºF) (24 Degree Celsius (ºC)) Temperature |
N/A 12 to 17 minutes |
Shear Strength |
N/A 50 psi |
Full Cure Time at 75 Degree Fahrenheit (ºF) (24 Degree Celsius (ºC)) Temperature |
N/A 24 hour |
Mixed Appearance with A19 |
N/A Tan Paste |
Mixed Appearance with A19 Black |
N/A Gray Paste |
Mixed Appearance with A19GB |
N/A Tan Paste |
Mixed Appearance with A19GB Red |
N/A Light Red Paste |
Mixed Appearance with A19GB Gray |
N/A Gray Paste |
Cured Appearance with A19 |
N/A Tan to Green |
Cured Appearance with A19 Black |
N/A Black |
Cured Appearance with A19GB |
N/A Tan to Green |
Cured Appearance with A19GB Red |
N/A Dark Red |
Cured Appearance with A19GB Gray |
N/A Gray |
Note for Typical Properties of Adhesive Mixed with Recommended Accelerator |
N/A Data is typical and not to be used for specification purposes. |
Typical Cured Properties
Tensile Strength at Break |
N/A 2700 psi18.6 MPa |
Test Method for Tensile Strength (Modified) |
N/A American Society for Testing and Materials (ASTM D638) |
Elongation |
N/A 30 % |
Test Method for Elongation (Modified) |
N/A American Society for Testing and Materials (ASTM D638) |
Young's Modulus |
N/A 130000 psi896.3 MPa |
Test Method for Young's Modulus (Modified) |
N/A American Society for Testing and Materials (ASTM D638) |
Glass Transition Temperature |
N/A 162 ºF72 ºC |
Test Method for Glass Transition Temperature (By Dynamic Mechanical Analysis (DMA)) |
N/A American Society for Testing and Materials (ASTM E1640-99) |
Bond Performance LORD® 406 Adhesive/LORD Accelerator 19
Lap Shear Strength at Room Temperature (Aluminum to Aluminum) |
N/A 3000 psi20.7 MPa |
Lap Shear Strength at Room Temperature (Galvanized Steel to Galvanized Steel) |
N/A 2500 psi17.2 MPa |
Lap Shear Strength at Room Temperature (Powder Coated Steel to Powder Coated Steel) |
N/A 2800 psi13.3 MPa |
Failure Mode for Lap Shear Strength at Room Temperature (Aluminum to Aluminum) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength at Room Temperature (Galvanized Steel to Galvanized Steel) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength at Room Temperature (Powder Coated Steel to Powder Coated Steel) |
N/A Cohesive Failure (C) |
Lap Shear Strength at Hot Strength (180 Fahrenheit (ºF) (82 Degree Celsius (ºC)) (Aluminum to Aluminum) |
N/A 1500 psi10.3 MPa |
Lap Shear Strength at Hot Strength (180 Fahrenheit (ºF) (82 Degree Celsius (ºC)) (Galvanized Steel to Galvanized Steel) |
N/A 1830 psi12.8 MPa |
Lap Shear Strength at Hot Strength (180 Fahrenheit (ºF) (82 Degree Celsius (ºC)) (Powder Coated Steel to Powder Coated Steel) |
N/A 1050 psi7.2 MPa |
Failure Mode for Lap Shear Strength at Hot Strength (Aluminum to Aluminum) |
N/A Thin Layer Cohesive Failure (TLC) |
Failure Mode for Lap Shear Strength at Hot Strength (Galvanized Steel to Galvanized Steel) |
N/A Thin Layer Cohesive Failure (TLC) |
Failure Mode for Lap Shear Strength at Hot Strength (Powder Coated Steel to Powder Coated Steel) |
N/A Coating Failure (CF) |
Lap Shear Strength after 500 Hours Salt Spray Exposure (Aluminum to Aluminum) |
N/A 2650 psi18.3 MPa |
Lap Shear Strength after 500 Hours Salt Spray Exposure (Galvanized Steel to Galvanized Steel) |
N/A 2500 psi17.2 MPa |
Lap Shear Strength after 500 Hours Salt Spray Exposure (Powder Coated Steel to Powder Coated Steel) |
N/A 1470 psi10.1 MPa |
Failure Mode for Lap Shear Strength after 500 Hours Salt Spray Exposure (Aluminum to Aluminum) |
N/A Thin Layer Cohesive Failure (TLC) |
Failure Mode for Lap Shear Strength after 500 Hours Salt Spray Exposure (Galvanized Steel to Galvanized Steel) |
N/A Thin Layer Cohesive Failure (TLC) |
Failure Mode for Lap Shear Strength after 500 Hours Salt Spray Exposure (Powder Coated Steel to Powder Coated Steel) |
N/A Coating Failure (CF) |
Lap Shear Strength after 14 Days at 100 Fahrenheit (ºF) (38 Degree Celsius (ºC)) Temperature and 100% Relative Humidity (RH) (Aluminum to Aluminum) |
N/A 2900 psi20.0 MPa |
Lap Shear Strength after 14 Days at 100 Fahrenheit (ºF) (38 Degree Celsius (ºC)) Temperature and 100% Relative Humidity (RH) (Galvanized Steel to Galvanized Steel) |
N/A 2450 psi16.9 MPa |
Lap Shear Strength after 14 Days at 100 Fahrenheit (ºF) (38 Degree Celsius (ºC)) Temperature and 100% Relative Humidity (RH) (Powder Coated Steel to Powder Coated Steel) |
N/A 2400 psi16.5 MPa |
Failure Mode for Lap Shear Strength after 14 Days (Aluminum to Aluminum) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength after 14 Days (Galvanized Steel to Galvanized Steel) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength after 14 Days (Powder Coated Steel to Powder Coated Steel) |
N/A Cohesive Failure (C) |
Lap Shear Strength at -30 Fahrenheit (ºF) (-34 Degree Celsius (ºC)) Temperature (Aluminum to Aluminum) |
N/A 3000 psi20.7 MPa |
Lap Shear Strength at -30 Fahrenheit (ºF) (-34 Degree Celsius (ºC)) Temperature (Galvanized Steel to Galvanized Steel) |
N/A 2800 psi19.3 MPa |
Lap Shear Strength at -30 Fahrenheit (ºF) (-34 Degree Celsius (ºC)) Temperature (Powder Coated Steel to Powder Coated Steel) |
N/A 3300 psi22.8 MPa |
Failure Mode for Lap Shear Strength (Aluminum to Aluminum) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength (Galvanized Steel to Galvanized Steel) |
N/A Cohesive Failure (C) |
Failure Mode for Lap Shear Strength (Powder Coated Steel to Powder Coated Steel) |
N/A Coating Failure (CF) |
T-Peel Strength (Aluminum to Aluminum) |
N/A 37 lb/in6.5 N/mm |
T-Peel Strength (Galvanized Steel to Galvanized Steel) |
N/A 22 lb/in3.9 N/mm |
T-Peel Strength (Powder Coated Steel to Powder Coated Steel) |
N/A 26 lb/in4.6 N/mm |
Failure Mode for T-Peel Strength (Aluminum to Aluminum) |
N/A Cohesive Failure (C) |
Failure Mode for T-Peel Strength (Galvanized Steel to Galvanized Steel) |
N/A Cohesive Failure (C) |
Failure Mode for T-Peel Strength (Powder Coated Steel to Powder Coated Steel) |
N/A Cohesive Failure (C) |
Substrate Material |
N/A Aluminum, 0.032" Thick 6061T6 Galvanized Steel, 0.030" Thick Electrogalvanized Powder Coated Steel, 0.035" Thick, Polyester on Cold Rolled Steel |
Surface Treatment for Aluminum |
N/A Dry Rag Wipe |
Surface Treatment for Galvanized Steel |
N/A Dry Rag Wipe |
Surface Treatment for Powder Coated Steel |
N/A Dry Rag Wipe |
Bonded Parameters |
N/A Metal Lap Shears (ASTM D1002) T-Peels (ASTM D1876 modified) |
Test Method for Metal Lap Shears |
N/A American Society for Testing and Materials (ASTM D1002) |
Test Method for T-Peel (Modified) |
N/A American Society for Testing and Materials (ASTM D1876) |
Bond Area for Metal Lap Shears |
N/A 1.0 x 0.5 in |
Bond Area for T-Peel |
N/A 1.0 x 3.0 in |
Film Thickness for Metal Lap Shears |
N/A 0.010 in |
Film Thickness for T-Peel |
N/A 0.010 in |
Cure Time at Room Temperature (RT) for T-Peel |
N/A 72 hour |
Mix Ratio By Volume for Metal Lap Shears |
N/A 4:1 |
Mix Ratio By Volume for T-Peel |
N/A 4:1 |
Note for Bond Performance |
N/A Bond performance data was obtained using LORD® 406 adhesive/Accelerator 19. Please contact LORD® Corporation regarding the use and/or performance of using other accelerator combinations (+1 877 ASK LORD®). |
Shelf Life/Storage
Shelf Life/Storage |
N/A Typical shelf life is nine months when stored below 80 ºF (27 ºC) in original, unopened container. Storage temperatures of 40-50 ºF (4-10 ºC) are recommended. If stored cold, allow product to return to room temperature before using. Protect from exposure |
Features
Versatile |
N/A Bonds a wide range of unprepared metals with minimal substrate preparation, as well as engineered thermoplastics including XENOY®, polycarbonate, ABS and acrylics. |
Temperature Resistant |
N/A Performs at temperatures from -40 ºF to +300 ºF (-40 ºC to +149 ºC). |
Environmentally Resistant |
N/A Resists dilute acids, alkalis, solvents, greases, oils, moisture, salt spray and weathering; provides excellent resistance to indirect UV exposure. |
Non-Sag |
N/A Remains in position when applied on vertical or overhead surfaces, allowing for greater process flexibility. |
Underwriters Laboratories (UL) Rated |
N/A When mixed with LORD® Accelerator 19, adhesive system is UL 746C certified. |
Applications
Surface Preparation1 | N/A Remove grease, loose contamination or poorly adhering oxides from metal surfaces. Normal amounts of mill oils and drawing compounds usually do not present a problem in adhesion. Most plastics require a simple cleaning before bonding. Some may require abrading for optimum performance. |
Mixing |
N/A Mix LORD® 403, 406 or 410 acrylic adhesive with the proper amount of LORD® Accelerator 19 or 19GB. Handheld cartridges will automatically dispense the correct volumetric ratio of each component. Even color distribution visually indicates a thorough mix. Once mixed, the adhesive cures rapidly. |
Curing |
N/A Cure begins immediately once adhesive and accelerator are mixed. Time to handling strength is dependent on adhesive used. Complete cure requires 24 hours at room temperature. Mating surfaces must be held in contact during the entire curing process. Cure rate can be accelerated by applying modest heat [<150 ºF (<66 ºC)]. Cured adhesive is colored to visually indicate a full cure; cure color depends on the accelerator used. |
Cleanup |
N/A Clean equipment and tools prior to the adhesive cure with solvents such as isopropyl alcohol, acetone or methyl ethyl ketone (MEK). Once adhesive is cured, heat the adhesive to 400 ºF(204 ºC) or above to soften the adhesive. This allows the parts to be separated and the adhesive to be more easily removed. |
Applying |
N/A
Apply adhesive using handheld cartridges or automatic meter/mix/dispense equipment.
|
Additional Information
Additional Information |
N/A
LORD® 403, 406 and 410 acrylic adhesives, when mixed with LORD® Accelerator 19 or 19GB, create adhesive systems that bond a wide variety of prepared or unprepared metals and engineered plastics. These adhesive systems are specifically formulated to provide the highest impact and peel strengths available in a room temperature curing adhesive. LORD® 403, 406 and 410 acrylic adhesives can be mixed with either LORD® Accelerator 19 or LORD® Accelerator 19GB. LORD® Accelerator 19 improves the high temperature resistance of LORD® 403, 406 and 410 acrylic adhesives, and is available in off-white or black. LORD® Accelerator 19GB allows precise control of the adhesive bondline thickness due to its content of glass beads. LORD® Accelerator 19GB is available in off-white, red or Gray. For further detailed information, refer to the LORD® Accelerator 19 and 19GB data sheet. Values stated in this technical data sheet represent typical values as not all tests are run on each lot of material produced. formalized product specifications for specific product end uses Information provided herein is based upon tests believed to be reliable. In as much as LORD® Corporation has no control over the manner in which others may use this information, it does not guarantee the results to be obtained. In addition, LORD® Corporation does not guarantee the performance of the product or the results obtained from the use of the product or this information where the product has been repackaged by any third party, including but not limited to any product end-user. Nor does the company make any express or implied warranty of merchantability or fitness for a particular purpose concerning the effects or results of such use. LORD® and "Ask Us How™" are trademarks of LORD® Corporation or one of its subsidiaries. LORD® provides valuable expertise in adhesives and coatings, vibration and motion control, and magnetically responsive technologies. Our people work in collaboration with our customers to help them increase the value of their products. Innovative and responsive in an ever-changing marketplace, we are focused on providing solutions for our customers worldwide. Ask Us How™. |
- 1 XENOY® is a trademark of General Electric Company