Qualified in accordance with:
EMBRAER : MEP 10-133, MEP 10-118

Product information mentioned in the technical datasheet is given for information purposes and can differ from requirements of specifications above. In that case, customer requirements are valid for your application.

P65-C2K primer can be applied directly on composite parts, suitably degreased and sanded.
All recommendations mentioned above are given for information.

Gloss levels have been determined using glossmeter with an angle of incidence of 60º. The theorical consumption value doesn’t take into account the transfer efficiency for spray application

Mixing ratio by weight - Base 100
Mixing ratio by volume - Base 4 V
Mixing ratio by weight - Hardener / Catalyst 24
Mixing ratio by volume - Hardener / Catalyst 1 V

Mixing Procedure - Ideally, the unmixed products should be stored between 18ºC and 25ºC (64ºF and 77ºF) for 24 hours before use.
The P65-C2K should be mixed for 5 to 10 minutes in a pneumatic or oscillating mixer before use.
Mix the base and the hardener until the mixture is homogeneous. The mixing must be made at a temperature between 15ºC (59ºF) and 35ºC (95ºF).
Sieve the paint through a 120-150 µm (4.5-6.0 mils) filter.

Induction Time - None

Spraying viscosity at 20ºC / 68ºF (Zahn 2 Cup) - 18 to 25s

Pot Life - 4 hours

Note
The paint viscosity may vary depending on the temperature and increase over the pot life.
Viscosities mentioned above are corresponding to the recommended range of viscosity to ensure compliant application. The range of dilution must be used to adjust

Mixing ratio by weight - Base 100
Mixing ratio by volume - Base 4 V
Mixing ratio by weight - Hardener / Catalyst 24
Mixing ratio by volume - Hardener / Catalyst 1 V

Mixing Procedure - Mix the base and hardener in proportions indicated above until the mixture is completely homogeneous.

Induction Time - None

Pot Life - 4 hours

Clean the equipment with a suitable cleaning solvent such as Mapaero D760. Mapaero D770-B aqueous cleaning solvent can also be used.

Apply 1 crossed coat to achieve a 15 µm to 25 µm (0.6 to 1 mil) dry thickness. Each coat has to be wet and of the same thickness.
The number of coats depends on the size and the shape of the part to be painted.
The recommended dynamic air pressure is 2 bar to 4 bar (30 to 60 psi).

Drying times have been determined using test pieces of 1 mm thickness, with a 20 µm (0.8 mils) dry film.
Before accelerated drying = 70ºC (158ºF), let it flash off for at least 15 minutes at room temperature.
Parts whose drying was forced must cool down to below 35 ºC (95ºF) before proceeding to the next step. To recoat P65-C2K primer with another product/primer, contact us.
For the P65-C2K primer infrared drying, contact us.
Drying time and temperature (evaporation and curing) are given for information only and may vary depending on humidity, the shape, the nature of the workpiece and the thickness of the paint.

In the event of a defect, contact your Quality Department.

For a dry thickness < 15µm (0.6 mils): Apply a thin layer to obtain the right thickness. If the recoating time is exceeded, reactivate with a Scotch-Brite type® A.

If there are micro-bubbles, running, rejects or numerous inclusions: Reactivate slightly, using an abrasive paper grade P240 or P320.
Remove dust using a suitable cloth and apply a thin coat of primer, as described above.

The P65-C2K is available in 5L (4L base and 1L hardener)

We guarantee our products against hidden defaults over material and preparation. Our Responsibility is limited to the obligation of freely replacing the defective material without there being a claim for any compensation. The advice we give is based on our experience but it might not be absolutely right. Consequently this does not imply our responsibility in case of inefficiency. Furthermore our company cannot be responsible for any material or corporal damages caused due to a misuse or mishandling of our products. Any concession to these clauses, to be valid, must be an official document issued by our offices and signed by our direction.