Part A Color |
N/A Gray |
Part B Color |
N/A White |
Mixed Color |
N/A Gray |
Part A Solids |
N/A 100 % |
Part B Solids |
N/A 100 % |
Mixed Solids |
N/A 100 % |
Part A Consistency |
N/A Paste |
Part B Consistency |
N/A Viscous Liquid |
Mixed Consistency |
N/A Thixotropic Paste |
Part A Density |
N/A 11.6 lb/gal |
Part B Density |
N/A 7.8 lb/gal |
Mixed Density |
N/A 11.4 lb/gal |
Part A Shelf Life at 77 Degree Fahrenheit (ºF) Temperature |
N/A 6 months |
Part B Shelf Life at 77 Degree Fahrenheit (ºF) Temperature |
N/A 6 months |
Mixing (Handling) |
N/A Part A and B must be mixed in the correct ratio and mixed thoroughly. Product is supplied in injection kits and comes with mixing instructions. Mechanical mixing is recommended. |
Recommended Mix Ratio by Weight (Part A/Part B) |
N/A 100/4.1 |
Recommended Mix Ratio by Volume (Part A/Part B) |
N/A 4.1/6.1 |
Working Life |
N/A Product will extrude from the tube nicely for 30 minutes after mixing. Product becomes tack free in 1 hour. |
Hardness |
N/A 50 Shore "A" |
Substrates Includes |
N/A Aluminum Primed Aluminum Stainless Steel Titanium |
Lap Shear Strength Control |
N/A 330 psi |
Lap Shear Strength after 7 Days at 400 Degree Fahrenheit (ºF) Temperature |
N/A 330 psi |
Lap Shear Strength after 7 Days at 120 Degree Fahrenheit (ºF) Temperature and 100% Relative Humidity (RH) |
N/A 330 psi |
Lap Shear Strength after 7 Days in BMS 3-11 Hydraulic Fluid |
N/A 260 psi |
Peel Strength |
N/A 20 lb/in |
Flame Resistance BMS 5-63 Rev. J |
N/A < 2 Seconds (sec) Self Extinguishing Time 0 Flame Penetration |
Applying |
N/A The substrate must be free from contamination, i.e. dirt, oil grease, etc. Clean the surface by wiping with a suitable solvent/cleaning agent and dry thoroughly. Handling strength is achieved in <4 hours at 72 ºF (25 ºC) (High loads on the product should |
Curing |
N/A DAPCO™ 2200 is generally cured at ambient temperatures above 55 ºF (13 ºC). Moisture helps develop final properties (a relative humidity ranging between 30-70% is preferred). Product reaches a hardness of 30 shore A in 4 hours at 72 ºF (22 ºC) and 50% R.H, allowing for quick repairs and fast "fly away" times. Full cure is achieved in 48 hours, however optimum physical properties are developed when the product is cured for seven days at 72 ºF (22 ºC) and 50% R.H. |
Cleanup |
N/A Before the material has cured, the excess may be removed using DAPCO™ 2000 diluent. |
Storage and Handling |
N/A
Shelf Life: 6 months when stored at or below 77 ºF (25 ºC) Keep in unopened foil bags. |
Features and Benefits |
N/A
|
Note |
N/A The information and statements herein are we believe to be reliable but are not to be construed as a warranty or representation for which Cytec Engineered Materials assumes legal responsibility. Users should undertake sufficient verification and testing to determine the suitability for their own particular purpose of any information or products referred to herein. No Warranty of Fitness for a Particular Purpose is Made. Nothing herein is to be taken as permission, inducement or recommendation to practice any patent invention without a license. |