EPIBOND® 1210 A-1 /9861 epoxy adhesive is a two-part paste which gives good properties at temperatures up to 300°F (149°C). This adhesive product is ideal for spacecraft applications due to its low out-gassing properties. EPIBOND® 1210 A-1 /9861 epoxy adhesive mixes to a semi-paste consistency and may be applied in glue lines of up to 50 mils for gap-filling applications. EPIBOND® 1210 A-1 /9861 epoxy adhesive bonds metals, composite laminates, most thermoplastics, rubbers and many other dissimilar materials. The epoxy adhesive is also available in different working life versions – EPIBOND® 1210 A-1/B and EPIBOND® 1210 A-1 /9861.
Brands |
N/A Epibond® Huntsman |
Tg (DMA) - Tand peak - Test Method Huntsman |
N/A 113 °C |
CTE - a1 Below transition - Test Method Huntsman |
N/A 53.5 ppm/°C |
CTE - a2 Above transition - Test Method Huntsman |
N/A 160.5 ppm/°C |
Test Method for Appearance |
N/A Visual |
Appearance |
N/A Tan |
Test Method for Density |
N/A ASTM D792 |
Density |
N/A 1.35 g/cm³ |
Viscosity at 77 Degree Fahrenheit (ºF) (25 Degree Celsius (ºC)) Temperature |
N/A Semi-Paste cP |
Original Equipment Manufacturer (OEM) Specifications |
N/A Lockheed Martin LAC 30-4639-0200, REV H/Loral 23-P12027-0003, REV 7 /Spectrolab 044418, REV A1 |
Minimum Gel Time/Pot Life at 77 Fahrenheit (ºF) Temperature |
N/A 35-60 (100 gram mass) minutes |
Suggested Cure Schedule Fahrenheit (ºF) |
N/A 48 hrs at 77 ºF or 1-2 hrs at 150 ºF |
Maximum Service Temperature |
N/A 250 ºF |
Lap Shear Strength at 77 Fahrenheit (ºF) Temperature (Aluminum to Aluminum) |
N/A 2,800 psi |
Lap Shear Strength at 180 Fahrenheit (ºF) Temperature (Aluminum to Aluminum) |
N/A 2,500 psi |
Flame Retardant |
N/A FALSE |
Packaging |
N/A Working packs |
Color |
N/A Tan |
First Aid |
N/A
Refer to SDS as mentioned above. |
Appearance - Mixed System - Test Method Visual |
N/A Tan |
Viscosity - Mixed System - Test Method ASTM D2196 |
N/A Semi-Paste cP |
Hardness, Shore D - Test Method ASTM D2240 |
N/A 88 |
Cure note |
N/A
Elevated temperature properties are improved with post cure of one hour at service temperature. |
Appearance - 1210 A-1 Resin - Test Method Visual |
N/A Tan |
Density - 1210 A-1 Resin - Test Method ASTM D792 |
N/A 1.49 g/cm³ |
Density - Mixed System - Test Method ASTM D792 |
N/A 1.35 g/cm³ |
Outgassing - TML - Test Method ASTM E595 |
N/A 0.77 % |
Outgassing - CVCM - Test Method ASTM E595 |
N/A 0 % |
Thermal Conductivity - Test Method C-Therm TCi |
N/A 0.5 W/mK |
Appearance - Hardener 9861 - Test Method Visual |
N/A Amber |
Density - Hardener 9861 - Test Method ASTM D792 |
N/A 1 g/cm³ |
Viscosity - 1210 A-1 Resin - Test Method ASTM D2196 |
N/A 250000 cP |
Viscosity - Hardener 9861 - Test Method ASTM D2196 |
N/A 16000 cP |
Gel Time, 100g at 77°F (25°C) |
N/A 35 - 60 min minutes |
Lap shear strength, Al-Al - 77°F (25°C) - Test Method ASTM D1002 |
N/A 2,800 (19.3) psi (MPa) |
Lap shear strength, Al-Al - 200°F (93°C) - Test Method ASTM D1002 |
N/A 2,500 (17.2) psi (MPa) |
Lap shear strength, Al-Al - 300°F (149°C) - Test Method ASTM D1002 |
N/A 500 (3.4) psi (MPa) |
Tg (DMA) - E’ Onset - Test Method Huntsman |
N/A 85 °C |
Tensile Strength - Test Method ASTM D638 |
N/A 8.6 (59.3) ksi (MPa) |
Tensile Modulus - Test Method ASTM D638 |
N/A 806.5 (5.6) ksi (GPa) |
Tensile Elongation - Test Method ASTM D638 |
N/A 1.3 % |
Flexural Strength - Test Method ASTM D790 |
N/A 15.4 (106.2) ksi (MPa) |
Flexural modulus - Test Method ASTM D790 |
N/A 811.3 (5.6) ksi (GPa) |
Lap Shear after fluid immersion - JP-4 - Test Method ASTM D1002 |
N/A 2,700 (18.6) psi (MPa) |
Lap Shear after fluid immersion - Skydrol - Test Method ASTM D1002 |
N/A 2,400 (16.5) psi (MPa) |
Lap Shear after fluid immersion - Distilled water - Test Method ASTM D1002 |
N/A 2,400 (16.5) psi (MPa) |
Mix Ratio |
N/A EPIBOND® 1210 A-1 Resin - Parts by weight: 100; Hardener 9861 - Parts by weight: 20 |
Mix Ratio Ritt by Weight |
N/A 100:20:00 |
Mix Ratio - EPIBOND® 1210 A-1 Resin - Parts by weight |
N/A 100 |
Mix Ratio - Hardener 9861 - Parts by weight |
N/A 20 |
Typical Cure Cycles |
N/A 48 hours at 77°F (25°C), or *Gel at room temperature + 1-2 hours at 150°F (66°C) |
Gel Time at 77 Degree Fahrenheit (ºF) Temperature |
N/A 35 - 60 min minutes |
|
N/A
EPIBOND® 1210 A-1 Resin / Hardener 9861 should be stored in a dry place in the original sealed containers at temperatures between 2°C and 40°C (36°F and 104°F). After use, tightly reseal containers. Under these storage conditions, and when supplied under Huntsman standard certification, the product has a shelf life of 1 year from date of shipment. The product should not be exposed to direct sunlight. |
|
N/A
Huntsman Advanced Materials Americas LLC maintains up-to-date Safety Data Sheets (SDS) on all of its products. These sheets contain pertinent information that you may need to protect your employees and customers against any known health or safety hazards associated with our products. Users should review the latest MSDS to determine possible health hazards and appropriate precautions to implement prior to using this material. |